파우더 종류에 따른 유분산 스틱제형의 마찰계수와 경도의 차이
Friction Coefficients and Hardness in oil dispersion stick Formulations by Various Powder types.
- 주제(키워드) 색조화장품 , 유분산
- 주제(DDC) 660.6
- 발행기관 아주대학교
- 지도교수 빈범호
- 발행년도 2022
- 학위수여년월 2022. 8
- 학위명 석사
- 학과 및 전공 일반대학원 응용생명공학과
- 실제URI http://www.dcollection.net/handler/ajou/000000032276
- 본문언어 한국어
- 저작권 아주대학교 논문은 저작권에 의해 보호받습니다.
초록/요약
Color cosmetics have recently developed into cosmetics that are commonly used regardless of gender and age because they can express the individuality of modern people, improve color, compensate for facial shortcomings, and highlight their strengths. With the development of color cosmetics, there are various types and formulations are also on the market. Among them, oil dispersion stick type cosmetics have been widely used for a long time, and are in high demand due to the advantages of Multi Proof and low stability issues. In this research, powder silica, Mica, and Talc of similar sizes were added to each of the three types of oil dispersion stick formulations, and then hardness, friction coefficient, and melting point were measured. Compared to each formulation, the hardness was measured to be the highest in the formulation using silica, followed by Mica and Talc. The hardness value of the silica-containing sample in the velvet formulation was about 1.58 gf, with Mica being 1.47 gf and Talc being 1.24 gf. The hardness value of the silica-containing sample in the matt formulation was about 1.2 gf, with Mica being 0.75 gf and Talc being 0.21 gf. The hardness value of the silica-containing sample in the glossy formulation was about 2.04 gf, with Mica of 1.92 gf and Talc of 1.63 gf. In the formulation using silica, the coefficient of friction was measured to be the highest, followed by Mica and Talc. The friction coefficient of the silica-containing sample in the velvet formulation was about 78.47 gf, with Mica being 63.27 gf and Talc being 55.38 gf. The friction coefficient of the silica-containing sample in the matt formulation was about 70.99 gf, with Mica being 63.66 gf and Talc being 60.45 gf. The hardness value of the silica-containing sample in the glossy formulation was about 55.37 gf, with Mica being 48.48 gf and Talc being 47.32 gf. The melting point was also measured the highest in the formulation using silica, followed by Mica and Talc. The melting point value of the silica-containing sample in the velvet formulation was about 70°C, with Mica at 69°C and Talc at 63°C. The melting point value of the silica-containing sample in the matt formulation was about 73°C, with Mica at 66°C and Talc at 55°C. The melting point value of the silica-containing sample in the glossy formulation was about 76°C, Mica was 70°C, and Talc was 61°C. Through this result, it was confirmed that there was a difference between the friction coefficient and hardness in the oil dispersion stick formulation according to the powder type.
more초록/요약
색조화장품은 현대인들의 개성을 표현할 수 있는 뿐 만 아니라 혈색을 개선시켜주고 얼굴의 단점을 보완하며 장점을 부각시켜 주는 장점이 있어 최근 남녀노소를 불문하고 흔히 사용하는 화장품으로 발전하게 되었다. 색조화장품의 발전으로 요즘은 종류도 다양하며 또한 제형도 다양하게 시장에 나와있다. 그 중 유분산 스틱형 화장품은 오래 전부터 널리 사용되었으며, Multi Proof의 장점과 안정성 이슈가 적어 수요가 많은 제형이다. 본 연구에서는 3가지 타입의 유분산 스틱 제형에 비슷한 사이즈의 파우더 Silica, Mica, Talc를 종류별로 투입하여 제조한 후 경도, 마찰계수, 녹는 점을 측정하였다. 각 제형별로 비교하였을 때 Silica를 사용 한 제형에서 경도가 가장 높게 측정되었으며, 그 다음은 Mica와 Talc 순 이였다. 벨벳 제형에서의 Silica함유 샘플의 경도 값은 약 1.58gf였으며 Mica는 1.47gf, Talc는 1.24gf였다. 매트 제형에서의 Silica함유 샘플의 경도 값은 약 1.2gf였으며 Mica는 0.75gf, Talc는 0.21gf였다. 글로시 제형에서의 Silica함유 샘플의 경도 값은 약 2.04gf였으며 Mica는 1.92gf, Talc는 1.63gf였다. Silica를 사용 한 제형에서 마찰계수도 가장 높게 측정되었으며, 그 다음은 Mica와 Talc 순 이였다. 벨벳 제형에서의 Silica함유 샘플의 마찰계수 값은 약 78.47gf였으며 Mica는 63.27gf, Talc는 55.38gf였다. 매트 제형에서의 Silica함유 샘플의 마찰계수 값은 약 70.99gf였으며 Mica는 63.66gf, Talc는 60.45gf였다. 글로시 제형에서의 Silica함유 샘플의 경도 값은 약 55.37gf였으며 Mica는 48.48gf, Talc는 47.32gf였다. Silica를 사용 한 제형에서 녹는 점 또한 가장 높게 측정되었으며, 그 다음은 Mica와 Talc 순 이였다. 벨벳 제형에서의 Silica함유 샘플의 녹는 점 값은 약 70℃였으며 Mica는 69℃, Talc는 63℃였다. 매트 제형에서의 Silica함유 샘플의 녹는 점 값은 약 73℃였으며 Mica는 66℃, Talc는 55℃였다. 글로시 제형에서의 Silica함유 샘플의 녹는 점 값은 약 76℃였으며 Mica는 70℃, Talc는 61℃였다. 이와 같은 결과를 통해 파우더 종류에 따라 유분산 스틱 제형에서 마찰계수와 경도의 차이가 보임을 확인하였다.
more목차
제1장 서론 1
제1절 색조 화장품 1
제2절 유분산 스틱형 화장품 2
제3절 연구목적 3
제2장 실험재료 및 방법 4
제1절 실험 재료 4
제2절 기기 및 장치 7
제3절 실험방법 8
제3장 결과 및 고찰 13
제1절 유분산 제형에서의 경도 측정 13
제2절 유분산 제형에서의 마찰계수 측정 16
제3절 유분산 제형에서의 녹는 점 23
제4장 결론 26
참고문헌 28