Stainless Steel Brake Disc의 마찰 마모특성에 관한 연구
- 발행기관 아주대학교
- 지도교수 박진일
- 발행년도 2013
- 학위수여년월 2013. 2
- 학위명 석사
- 학과 및 전공 산업대학원 기계공학과
- 실제URI http://www.dcollection.net/handler/ajou/000000013807
- 본문언어 한국어
- 저작권 아주대학교 논문은 저작권에 의해 보호받습니다.
초록/요약
This study verified the corrosion resistance of stainless steel brake disk how much improvement has been compared with conventional gray cast iron discs through a salt spray test. And then verified quantitatively falling of wear and friction performance due to the lack of thermal properties of stainless steel through a scale dynamometer, consequently compared to gray cast iron friction performance showed a similar trend but wear was increased. Low thermal conductivity and specific heat capacity of the stainless steel focused on the local and destroyed by the transfer layer is thought to be an increase in wear rate. In order to verify the heat treatment on the friction performance and wear resistance, three type of hardness of heat treatment stainless steel disc of experiments were performed. As a result, it was confirmed that the friction performance and wear resistance equivalent to the level of conventional gray cast iron in the samples of highest hardness HRc45. Considering in this study used the friction material optimized gray cast iron, apply to friction material suitable for stainless steel in the future, it is expected to show the wear performance than gray cast iron.
more목차
논문 요약 ⅲ
Abstract ⅳ
표 목차 ⅴ
그림 목차 ⅵ
Ⅰ. 서 론 1
1. 연구의 필요성 및 연구 방향 1
2. 배경 이론 4
2.1 자동차 브레이크 시스템 4
2.2 마찰 6
2.2.1 마찰의 정의 6
2.2.2 응착마찰 이론 7
2.2.3 마모발생기구 8
2.3 부식 12
2.3.1 부식의 정의 12
2.3.2 부식의 종류 12
Ⅱ. 본 론 18
1. 실험방법 18
1.1 내식성 비교 실험 18
1.1.1 실험 절차 18
1.2 마찰시험 20
1.2.1 마찰 시편 제작 20
1.2.2 마찰 시험 및 평가 22
2. 실험결과 24
2.1 내식성 24
2.2 마찰특성 27
2.2.1 버니쉬 시험 27
2.2.2 온도별 마찰 특성 29
2.3 마모 특성 32
2.3.1 디스크의 온도별 마모 특성 32
2.3.2 마찰재의 온도별 마모 특성 36
Ⅲ. 결 론 38
Reference 39